p Effect of crosslink structure on mechanical properties, thermal stability and flame retardancy of natural flavonoid based epoxy resins

编号 020033905

推送时间 20220418

研究领域 林产化工 

年份 2022 

类型 期刊 

语种 英语

标题 p Effect of crosslink structure on mechanical properties, thermal stability and flame retardancy of natural flavonoid based epoxy resins

来源期刊 European Polymer Journal

期 第339期

发表时间 20220105

关键词 Bio-based epoxy resin;  Crosslink density;  Mechanical properties;  Thermal stability; 

摘要 Three novel bio-based epoxy resins were synthesized based on natural flavonoids (daidzain, naringenin and luteolin). Maleic anhydride was used as curing agent. The effect of crosslink structure on mechanical properties, thermal stability and flame retardancy of bio-based epoxy resins was investigated. The results showed that the mechanical properties of bio-based epoxy resins were significantly better than that of di-glycidyl ether of bisphenol A, but the flame retardancy of bio-based epoxy resins was not significantly improved compared with di-glycidyl ether of bisphenol A. The cycloaddition reaction of benzopyrone ring is conducive to the formation of high crosslink density. The mechanical properties and thermal stability of bio-based epoxy resins increased with increasing crosslink density. The impact strength and initial thermal degradation temperature of cured daidzein epoxy resin which with the highest crosslink density were 0.86 kJ/m2 and 22 degrees C higher than that of di-glycidyl ether of bisphenol A, respectively. The glass transition temperature of cured daidzein epoxy resin was 184.4 degrees C.

服务人员 尚玮姣

服务院士 宋湛谦

PDF文件 浏览全文