Biorenewable rosin derived benzocyclobutene resin: a thermosetting material with good hydrophobicity and low dielectric constant



编号 020020904

推送时间 20191021

研究领域 林产化工 

年份 2019 

类型 期刊 

语种 英语

标题 Biorenewable rosin derived benzocyclobutene resin: a thermosetting material with good hydrophobicity and low dielectric constant

来源期刊 RSC ADVANCES

第209期

发表时间 20190914

关键词 CROSS-LINKING;  POLYMER;  TEMPERATURE;  NANOINDENTATION;  NANOPARTICLES;  EFFICIENT;  CELLULOSE;  ETHER;  ACID;  OIL; 

摘要 Development of bio-based polymers has been promoted by the growing concerns about the long-term sustainability and negative environmental footprint of petroleum-based polymer materials. A new monomer containing benzocyclobutene and allyl units has been developed by using rosin as the feedstock. The structure of the monomer was characterized by elemental analysis, MS, FT-IR and NMR spectroscopy. The monomer could be converted to the polymer via thermal ring-opening polymerization which was characterized via FT-IR, thermogravimetric analysis (TGA), atom force microscopy (AFM) and so on. The polymer showed good dielectric properties and hydrophobicity with an average dielectric constant of 2.51 in a range of frequencies from 0.1 to 18 MHz and a water contact angle of 106 degrees. In addition, the polymer with other comprehensive performances exhibited a 5% weight loss temperature of 406 degrees C, a surface roughness (R-a) of 0.658 nm in a 5.0 x 5.0 mu m(2) area, hardness and Young's modulus of 0.283 and 3.542 GPa, and storage modulus of 11.46 GPa at 30 degrees C. These data suggest that the polymer may have potential application in electronics and microelectronics.

服务人员 尚玮姣

PDF文件 浏览全文

相关图谱

扫描二维码