Sustainable alternative for bisphenol A epoxy resin high-performance and recyclable lignin-based epoxy vitrimers



编号 020031605

推送时间 20211108

研究领域 林产化工 

年份 2021 

类型 期刊 

语种 英语

标题 Sustainable alternative for bisphenol A epoxy resin high-performance and recyclable lignin-based epoxy vitrimers

来源期刊 Industrial Crops & Products

第316期

发表时间 20210430

关键词 Lignin;  Epoxy vitrimers;  Self-healing;  Shape memory polymer; 

摘要 Epoxy vitrimers based on dynamic covalent bond chemistry have been developed in recent years as they can solve the problem of recycling and reuse for traditional thermosetting materials. Lignin as an aromatic raw material has recently used to partially replace commercial diglycidyl ether bisphenol A (DGEBA) in the epoxy vitrimers, however, it is difficult to achieve high lignin replacement rate, excellent mechanical property and reprocessability in a facile method at the same time. In this work, high mechanical strength and lignin replacement rate of lignin-based vitrimers were successfully synthesized by gradually replacing DGEBA with glycidyl ether of lignin. The mechanical properties of the lignin-based epoxy vitrimers can be tuned by different ratios of glycidyl ether of lignin and DGEBA, the Young’s modulus and tensile strength of those vitrimers can reach up to 2.00 GPa and 46.8 MPa, respectively. It's worth noting that the tensile strength and elongation at break were 39.5 MPa and 5.81 % when the lignin replacement rate was 100 %. All the lignin-based epoxy vitrimers exhibit excellent self-healing, reprocessing and shape memory property. The crack widths of the vitrimers were repaired over 80 % in just 5 min at 160 ℃, the tensile strength can reach up to 97 % healing efficiency after being hot reprocessed. The great properties of lignin-based epoxy vitrimers indicate that they can be used as renewable alternatives for bisphenol A epoxy vitrimers.

服务人员 尚玮姣

服务院士 宋湛谦

PDF文件 浏览全文

相关图谱

扫描二维码