Multiway Softness Polyurethane Elastomeric Composite with Enhanced Thermal Conductivity and Application as Thermal Interface Materials

编号 020038402

推送时间 20230227

研究领域 林产化工 

年份 2022 

类型 期刊 

语种 英语

标题 Multiway Softness Polyurethane Elastomeric Composite with Enhanced Thermal Conductivity and Application as Thermal Interface Materials

来源期刊 ADVANCED MATERIALS TECHNOLOGIES

期 第384期

发表时间 20230201

关键词 aluminum;  dynamic covalent bonds;  polyurethane elastomer composites;  thermal interface materials; 

摘要 The ever-increasing computing power in modern electronics comes with significant heat waste that can't be ignored. For microchips to dissipate heat efficiently, thermal interface materials (TIMs) are the most critical components in semiconductor packaging. Soft elastomer composites are often used as TIMs due to their large-strain reversible deformability with a small external force. For TIMs to cushion between the microchip and heat spreader, they must have high thermal conductivity and temperature-tunable softness to reduce thermal resistance and relieve the warpage failure caused by thermal stress. However, thermal conductivity and softness are interrelated and restrict each other. To address this challenge, a radical strategy of introducing dynamic covalent bonds in the polyurethane/aluminum composite is used. The reversible and low energy of dynamic imine bonds along with the lengthening of the Khun segment in the crosslinking network imbues the material with temperature-tunable softness function while maintaining high thermal conductivity. The resulting polyurethane elastomer (PUE) composite exhibits remarkable thermal conductivity (6.90 W m(-1) K-1), low thermal resistance (0.13 K cm(2) W-1), and excellent softness (elastic modulus 759.50 kPa, and stretchability 140.30%). This work provides a practical method to design thermally conductive and temperature-tunable soft elastomer composites as TIMs in semiconductor packaging.

服务人员 尚玮姣

服务院士 宋湛谦

PDF文件 浏览全文