A Conceptional Approach of Resin-Transfer-Molding to Rosin-Sourced Epoxy Matrix Green Composites



编号 020028202

推送时间 20210315

研究领域 林产化工 

年份 2021 

类型 期刊 

语种 英语

标题 A Conceptional Approach of Resin-Transfer-Molding to Rosin-Sourced Epoxy Matrix Green Composites

来源期刊 Aerospace

第282期

发表时间 20201228

关键词 rosin-sourced anhydrite;  epoxy;  viscosity;  LCM process;  carbon fiber composite;  ramie fiber composite;  in-plane mechanical properties; 

摘要 In this concept-proof study, a preform-based RTM (Resin Transfer Molding) process is presented that is characterized by first pre-loading the solid curing agent onto the preform, and then injecting the liquid nonreactive resin with an intrinsically low viscosity into the mold to infiltrate and wet the pre-loaded preform. The separation of resin and hardener helped to process inherently high viscosity resins in a convenient way. Rosin-sourced, anhydrite-cured epoxies that would normally be regarded as unsuited to liquid composite molding, were thus processed. Rheological tests revealed that by separating the anhydrite curing agent from a formulated RTM resin system, the remaining epoxy liquid had its flowtime extended. C-scan and glass transition temperature tests showed that the preform pre-loaded with anhydrite was fully infiltrated and wetted by the liquid epoxy, and the two components were diffused and dissolved with each other, and finally, well reacted and cured. Composite laminates made via this approach exhibited roughly comparable quality and mechanical properties with prepreg controls via autoclave or compression molding, respectively. These findings were verified for both carbon and ramie fiber composites.

服务人员 尚玮姣

服务院士 宋湛谦

PDF文件 浏览全文

相关图谱

扫描二维码