Rosin-derived poly(vinyl chloride) plasticizer: Synthesis, structure, and properties

编号 020020101

推送时间 20190826

研究领域 林产化工 

年份 2019 

类型 期刊 

语种 英语

标题 Rosin-derived poly(vinyl chloride) plasticizer: Synthesis, structure, and properties

来源期刊 JOURNAL OF VINYL & ADDITIVE TECHNOLOGY

期 第201期

发表时间 20190709

关键词 OIL-BASED PLASTICIZER;  SOYBEAN-OIL;  THERMAL-STABILITY;  FLAME RETARDANCY;  PVC;  PHOSPHATE;  MECHANISM;  BEHAVIOR; 

摘要 In this work, rosin-based plasticizer was synthesized by Diels-Alder (DA) and esterification. First, the maleopimaric acid (RT) was obtained by DA between the double bond of rosin and maleic anhydride. Then, the carboxyl group and anhydride group of RT was esterified with tetrahydro geraniol to obtain the rosin-based polyacid esters (RTT) under the catalysis of p-toluene sulfonic acid. The structure of RT and RTT was detected by FTIR and H-1-NMR. RTT was used as main plasticizer to obtain plasticized polyvinyl chloride (PVC) materials and compared with DOP. The results showed that RTT improved the thermal stability and reduced T-g of PVC film. Plasticized PVC films had excellent mechanical properties with the elastic modulus of -4,793.67 MPa and tensile strength of -111.86 MPa, higher than that of pure PVC and DOP-6. RTT showed better volatility stability, migration, and solvent extraction in PVC compared to DOP.

服务人员 尚玮姣

PDF文件 浏览全文