Highly efficient phosphorous-containing flame retardant for transparent epoxy resin with good mechanical properties



编号 020038205

推送时间 20230213

研究领域 林产化工 

年份 2022 

类型 期刊 

语种 英语

标题 Highly efficient phosphorous-containing flame retardant for transparent epoxy resin with good mechanical properties

来源期刊 Journal of Polymer Research

第382期

发表时间 20221223

关键词 DOPO;  Piperazine;  Flame retardant;  Transparency;  Mechanical property; 

摘要 To develop transparent flame-retardant epoxy resin (EP) having good mechanical properties, a 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO) derived flame retardant (PAHDOPO) was prepared by a neutralization reaction between 10-hydroxy-9, 10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO-OH) and piperazine. When 7% PAHDOPO was added to EP, the obtained flame-retardant EP (EP7) can pass the UL-94 V-0 rating test and exhibit a high limiting oxygen index (LOI) value of 35.8%. Microscale combustion calorimetry investigation results proved that, compared with EP, the peak heat release rate (PHRR) and heat release capacity (HRC) of EP7 decreased by 34.6% and 33.6%, respectively. The observation of the char residue morphology indicated that the addition of PAHDOPO can lead to the formation of the continuous and dense char residue layer, which can improve EP flame retardancy. Meanwhile, compared with EP, EP7 exhibited similar transparency with less than 8% reduction in the average transmittance. Moreover, the mechanical properties of EP7 hardly decreased in comparison with EP. All these results indicated that PAHDOPO can be applied as a high-performance flame retardant of EP with good mechanical properties, transparency, and flame retardancy simultaneously.

服务人员 尚玮姣

服务院士 宋湛谦

PDF文件 浏览全文

相关图谱

扫描二维码