Preparation and research of epoxy modified by carboxyl-terminated polybutylene adipate at room temperature



编号 020035802

推送时间 20220829

研究领域 林产化工 

年份 2022 

类型 期刊 

语种 英语

标题 Preparation and research of epoxy modified by carboxyl-terminated polybutylene adipate at room temperature

来源期刊 RSC Advances

第358期

发表时间 20220715

关键词 NANOFILLERS;  IMPROVEMENT;  RESIN; 

摘要 In this study, carboxyl-terminated polybutylene adipate (CTPBA) was used to modify epoxy resin, and the modified epoxy resin was cured by a room temperature rapid curing agent (T-31). The effects of CTPBA modification on bonding properties and mechanical properties of epoxy resin adhesive at room temperature were carefully studied. Epoxy-terminated prepolymer was synthesized by pre-polymerization and its structure was characterized. Compared with the addition method of direct blending, the bonding properties and mechanical properties of pre-polymerized epoxy resin adhesive were significantly better. Compared with unmodified epoxy resin, CTPBA modification significantly improved the bonding strength. Furthermore, with the increase of CTPBA content, the shear strength of the material increased first and then decreased, and reached the maximum when the addition amount was 40 phr. This shows that the tensile strength of the material decreased with the increase of CTPBA content, and the elongation at break increased with the increase of CTPBA content. Dynamic mechanical analyzer (DMA) test results showed that the addition of CTPBA reduced the glass transition temperature, but broadened the damping temperature range. TG analysis showed that the thermal stability of the modified epoxy resin was good, and compared with pure epoxy resin, the initial temperature of thermal weight loss and the maximum thermal decomposition rate decreased, but the overall thermal stability was not significantly different. In summary, CTPBA modification of epoxy resin is expected to improve the comprehensive mechanical properties at room temperature.

服务人员 尚玮姣

服务院士 宋湛谦

PDF文件 浏览全文

相关图谱

扫描二维码